@Kyresti @starkatt Too much carbon, or just too much work-hardening, and your steel will shatter instead of bend. Pretty sure excessive phosphorus will ruin a steel too, but you're more likely to get a bunch of carbon added while welding than phosphorus. Unless you're using some *very* inadvisable fuel for torch welding.
-F